Characterization of the surface quality defects in cast frameworks for Cobalt – Chrome dental prostheses
Introduction: Cobalt – Chromium alloys have been used for the fabrication of cast frameworks which withstand the dental prostheses, failures that happen during the process of casting, polishing and finishing the framework generate surface quality defects which affect the mechanical properties of dentures.
Objective: To characterize the surface quality defects in cast frameworks for Cobalt – Chrome dental prostheses by scanning electron microscopy (SEM).
Materials and Methods: An experimental study was conducted, where 19 cast frameworks made out of Cobalt – Chrome alloy were conveniently selected. The following variables were taken into account during the casting process: presentation of the alloy, type of centrifugal casting, way of polishing, shining and sanding the framework. Results: The main characteristics observed, by scanning electron microscopy (SEM) analysis, in the cast frameworks for Cobalt – Chrome dental prostheses were: irregularities, superficial heterogeneity, presence of carbon and cracks. There was also found a statistically significant association between the presentation of the alloy and the polishing with shinning and without shinning, with a value of p (0,04).
Conclusions: Characterization by scanning electron microscopy (SEM) allows us to detect surface quality defects which generate mechanical failures and damages within medium and long term use, affecting the quality of dental prostheses.
How to Cite
License
Every single author of the articles has to declare that is an original unpublished work exclusively created by them, that it has not been submitted for simultaneous evaluation by another publication and that there is no impediment of any kind for concession of the rights provided for in the contract.
In this sense, the authors committed to await the result of the evaluation by the journal Revista Nacional de Odontologia before considering its submission to another medium; in case the response by that publication is positive, additionally, the authors committed to respond for any action involving claims, plagiarism or any other kind of claim that could be made by third parties.
At the same time, the authors have to declare that they are completely in agreement with the conditions presented in their work and that they cede all patrimonial rights. These rights involve reproduction, public communication, distribution, dissemination, transformation, making it available and all forms of exploitation of the work using any medium or procedure, during the term of the legal protection of the work and in every country in the world, to the Universidad Cooperativa de Colombia Press.
GUZMAN BAEZ, Humberto José. Biomateriales odontológicos de uso clínico. Quinta edición, Santa Fe de Bogotá: Ecoe ediciones, 2013.
. SKINNER J. La ciencia de los materiales dentales. Undécima edición, ELSEVIER 2004.
. CRAIG, Robert. Materiales de odontología restauradora. Décima edición, Madrid: Harcourt – Brace, 1998.
. Harcourt M. Propiedades de los biomateriales materiales de odontología restauradora.1998. Madrid.
. Rivas, M. A., & María, A. (2001). Evaluación visual y radiográfica de discontinuidades en estructuras metálicas de prótesis parciales removibles. Acta Odontológica Venezolana, 39(2), 25-34.
. Borrás, V. A., Paolini, A., Ballester, J. M., Escuder, A. V., & Sanchis, F. R. (2002). Estudio de la influencia de los
tratamientos térmicos en la microdureza y microestructura de aleaciones Co-Cr-Mo. In Congreso Nacional de Propiedades Mecánicas de Sólidos, Gandia (pp. 487-496).
. Fomaro, J. G. Microstructural evolution during solution treatment of Co–Cr–Mo–C biocompatible alloys. 2012. 9.
. Elamin A. Elarbi, Yahia H. Ismail, Mohsen Azarbal, Tarnjit S. Saini, Radiographic detection of porosities in removable partial denture castings. The Journal of Prosthetic Dentistry volumen 54. N° 5 de 1985.
. Echeverri, A. Caracterización metalográfica de barras para sobre dentaduras, elaboradas por sobre colado de pilares para implantes dentales. Revista de la Facultad de Odontología Universidad de Antioquia. 2013.
. Sunder Dharmar, R. Radiographic and metallographic evaluation of porosity defects and grain structure of cast chromium cobal removable partial dentures. The Journal of Prosthetic Dentistry, 369-373. 1993.
. Vordos, C. V. Efecto de la refundición en las propiedades mecánicas de las aleaciones de cromo-cobalto. Recuperado el 18 de Julio de 2014, de Scopus.
. García, J. Caracterización microestructural de aleaciones coladas Al-7 Si-Cu Al-7 Si-Ni con adiciones de Sr. Revista latinoamericana de metalurgia y materiales. 2003.
. Hae Ri Kim, Young Kyung Kim, Jun Sik Son, Bong Ki Min, Kyo-Han Kim, Tae-Yub Kwon. Comparison of in vitro biocompatibility of a Co–Cr dental alloy produced by new milling/post-sintering or traditional casting technique. Materials Letters, 2016; 178:300-303.ISSN0167-577http://dx.doi.org/10.1016/j.matlet.2016.05.053.
Disponible(http://www.sciencedirect.com/science/article/pii/S0167577X16307881.
. B. Qian, K. Saeidi, L. Kvetková, F. Lofaj, C. Xiao, Z. Shen. Aleaciones dentales Co-Cr-Mo Defectos tolerantes preparados por fusión selectiva por láser. Materiales Dentales. 2015; 31(12):1435-1444.ISSN0.109-5.641, http://dx.doi.org/10.1016/j.dental.2015.09.003. Disponible (Http://www.sciencedirect.com/science/article/pii/S0109564115003991.
. Anjin Lu, Songquan Wu, Yiliang Gan, Junlei Li, Chaoqian Zhao, Dongxian Zhuo, Jin Xin Lin. Investigación sobre la microestructura, propiedades mecánicas y el comportamiento a la corrosión del selectivo por láser funde la aleación Co Cr W para aplicación dental. Ciencia de los Materiales e Ingeniería. 2015; 49:517-525. ISSN 0928 hasta 4931, http://dx.doi.org/10.1016/j.msec.2015.01.023. Disponible (Http://www.sciencedirect.com/science/article/pii/S0928493115000338.
. Y.S. Al Jabbari, T. Koutsoukis, X. Barmpagadaki, S. Zinelis. Metalúrgica y caracterización de aleaciones dentales interfacial PFM Co-Cr fabricado mediante fundición, de la molienda o de fusión selectiva por láser. Materiales Dentales; 2014 30(4): E79-E88,http://dx.doi.org/10.1016/j.dental.2014.01.008. disponible
(Http://www.sciencedirect.com/science/article/pii/S0109564114000207).
. Bauer J, Costa JF, Carvalho CN, Miranda RE, Dourado A, Reis A. Caracterización de dos aleaciones dentales de Ni-Cr y la influencia del modo de colada en las propiedades mecánicas, Diario de Prosthodontic Research. 2012; 56 (4): 264-271, ISSN 1883-1958, http://dx.doi.org/10.1016/j.jpor.2012.02.004. Disponible (Http://www.sciencedirect.com/science/article/pii/S1883195812000333).
. P. Mengucci, G. Barucca, A. Gatto, E. Bassoli, L. Denti, F. Fiori, E. Girardin, P. Bastianoni, B. Rutkowski, A. Czyrska-Filemonowicz, Efectos de los tratamientos térmicos en la microestructura y mecánico propiedades de una aleación biomédica Co-Cr-Mo-W producido por sinterización láser. Diario del comportamiento mecánico de materiales biomédicos. 2016; 60: 106-117, ISSN 1751 a 6161, http: //dx.doi. org / 10.1016 / j. jmbbm.2015.12.045. Disponible (Http://www.sciencedirect.com/science/article/pii/S1751616116000023).
. M. Walczak, K. cerveza, B. Surowska, J. Borowicz. El tema del uso de aleaciones de Co Cr Mo refundidos en prótesis dentales. Archivos de ingeniería civil y mecánica. 2012;12 (2):171-177, ISSN 1644 -9665, http://dx.doi.org/10.1016/j.acme.2012.04.001. Disponible (Http://www.sciencedirect.com/science/article/pii/S1644966512000301).
. McGinley EL, Coleman DC, Gary, Moran P, Garry JP. Efectos de las condiciones de acabado de superficie sobre la biocompatibilidad de una aleación de fundición de níquel-cromo dental. Dental Materials.2011; 27(7): 637- 650, ISSN 0109 hastas 5641, http://dx.doi.org/10.1016/j.dental.2011.03.004. (Http://www.sciencedirect.com/science/article/pii/S0109564111000741).
. Henriques B, Faria S, Soares D, Silva FS. Efecto del calor de presión sobre la resistencia al cizallamiento de la porcelana dental para sustratos de aleación Co Cr Mo Si con diferentes tratamientos superficiales. Ciencia de los Materiales e Ingeniería. 2013; 33(1):557-563. ISSN desde 0928 hasta 4931, http://dx.doi.org/10.1016/j.msec.2012.10.001. (Http://www.sciencedirect.com/science/article/pii/S092849311200464X).
. Kenta Y, Manami M, Akihiko. Efectos de la concentración de carbono en la microestructura y las propiedades mecánicas de los recién colado aleaciones libres de níquel-base-28Cr-9W Co dentales. Ciencia de los Materiales e Ingeniería.2014; 40(1): 127-134, ISSN 0928 a 4931, http://dx.doi.org/10.1016/j.msec.2014.03.053. Disponible (Http://www.sciencedirect.com/science/article/pii/S0928493114001799).